Hello all,
When fired, should white bronze be bendable? Obviously stiff and solid is a given, but should it snap at a weak area or bend?
I fired a piece and, when putting some pressure on the bail to check the strength, it snapped off.
If it was just too thin, would it have bent rather than snapped?:
I followed the instructions to the letter - 15 mins at 500 degrees C on coconut carbon in a stainless steel container, then 2 hours at 770 degrees C with a layer of carbon on top and the lid on the container.
Any help would be appreciated,
Thank you in advance :-)