Brooch Commission.

[FloWolF]

A commission I'm working on for my wonderful aunt, who's ordered it as a 60th gift for her sister, hence the 6 separate pieces - one for each decade.

Made from pine cone and crushed oyster shell cast in urethane resin, coloured burgundy.

[FloWolF]

0.8mm sterling wire, slightly flattened then shaped - this should solder onto the silver base, then I can 'artistically adjust' the loop shapes to hold the cabochons - there's 3 more flattened and looped wire pieces to sit in the middle to hold the other sides of the cabs too but haven't taken pics of those yet.







Brooch pin is made from 1.5mm sterling wire, hammered into a pin shape before torsioning/twisting to further harden it, then slightly fettled with sandpaper to remove any roughness.





Now it just needs soldering... the bit I'm most scared of here because that wire is gonna be tough to do without it all going to sh*t in the blink of an eye!

So far everything's been soldered in hard grade, so the wire I'll do next in medium, then attach the pin mount using easy grade and hope everything stays where I put it...

I may do this tonight, if not tomorrow if I have the time - wish me luck please I'm cr*pping ('scuse) myself as I've quite a few hours sunk into this already!

Cheers, hope everyone is well! ',;~}~

Shaun/FloWolF

[metalsmith]

Gentle heating and it'll all go swimmingly. Pins don't have to be silver btw.

[FloWolF]

Gentle heating and it'll all go swimmingly. Pins don't have to be silver btw.

Thanks I'll do my best - I've ruined a few pieces during soldering because I get nervous, then I get distracted, and I blink and then it's silver puddle time...

As for the pin yes I'm aware they don't need to be silver and that a lot of people use stainless because of how silver is difficult to harden sufficiently, but that's why I wanted to do it in silver! I figured if it didn't work then I'd do another in stainless quickly enough. As it is the pin works perfectly after the hammer and twist treatment, and I don't believe it's too thick after hammering it into a gradual taper - at the thickest it's about 1.25mm I think.

Thanks again,

Shaun/FloWolF

[Dennis]

Its cliff hanger. I'm waiting to see the finished piece.
I would mention here Shaun, that heavy pins leave permanent holes in clothing (unless it is thick knitwear) so not always appreciated.
The thickest pin I would use here is about 0.8mm.
I would also probably solder on the brooch fitting next, and the retentive loops last, because they are the most likely to give trouble if re- heated. Dennis.

[FloWolF]

Its cliff hanger. I'm waiting to see the finished piece.
I would mention here Shaun, that heavy pins leave permanent holes in clothing (unless it is thick knitwear) so not always appreciated.
The thickest pin I would use here is about 0.8mm.
I would also probably solder on the brooch fitting next, and the retentive loops last, because they are the most likely to give trouble if re- heated. Dennis.

This was my thinking initially too Dennis, but I tend to struggle with the easy solder flowing right on more delicate joints, but not so with larger areas like the pin mount, added to this it's easier for me to arrange it flat for soldering the wire 'retainer' on before the pin mount is in place on the back, and I was suddenly less sure if that was the best order after all, and I considered I could use wetted tissue or sand, or even the heat resist paste I bought from Cookson's to help protect the wire, and do the mount last instead. So even weighing your reply in, I still haven't arrived at a conclusion unless you've anything further to add?

As for the pin thickness I'd read your own advice in previous threads, and I've had pin damaged clothing myself so I do understand the point (scuse the pun!) fully. I'll measure this pin tomorrow as the 1.25mm was just a guess, but the thickest part of the length can't be much more than 1mm, with the majority tapering to well under that.

Thanks for looking in Dennis your experience is always appreciated.

G'night,

Shaun/FloWolF