Ring soldering advice
Hi all,
I'm making wedding bands out of a meteorite. I'm about done forging the bars, so I'm almost ready to start shaping. I've got rods for each of the ring sizes to bend the bars around, but I'm unsure as to what solder would be best to use to close the ends.
The meteorite is about 92% iron, 8% nickel with some other trace bits. I'm thinking silver solder would probably blend the best, but I don't know anything so my opinion isn't worth much! Can anyone offer any advice what to use? Thanks.