I don't know why I feel so strongly, but I do.

When we heat treat stone to improve the color etc. we use temperatures in the 400 to 600 range. I keep seeing stons destroyed by soldering or worse setting them in PMC and firing.

The problem is, the books I read are advocating it! Sure why not have a lottery!

Sorry but something had to be said

Julian