I don't think there is really an ideal , just the lowest temp you can get a complete casting from. With my kiln which may not be calibrated I can go down to 530 ish for heavy stuff and If its lots of filigree type work as much as 600 ish. Sorry I cant be more specific but its a bit of trial and error to find the perimeters. You should be able to pickle the black off the casting.