  1. Replies
    6
    Views
    175

    I wouldn't be happy with that its a bad cast.

    I wouldn't be happy with that its a bad cast.
  2. Replies
    6
    Views
    175

    When you say it was printed in wax do you know...

    When you say it was printed in wax do you know which machine was used ? How big was it approx. Sometimes you do get holes and things this is especially true from resin prints( I know you said wax) of...
  3. Thread: Issue soldering

    by josef1
    Replies
    2
    Views
    137

    You may need more heat depending on the size of...

    You may need more heat depending on the size of the bangle more metal requires a bigger torch.
  4. Replies
    29
    Views
    558

    Thankyou. I'm not really open at the moment just...

    Thankyou. I'm not really open at the moment just doing odd days. But I could make it yes, if you sourced the stone and can wait till things get a bit more normal.
  5. Replies
    6
    Views
    174

    Rhodium solution is at an high at the moment...

    Rhodium solution is at an high at the moment around 800 a litre last time I checked. It looks great but you would need to do lots of jewellery to recover your money. Maybe look at a product called...
  6. Replies
    29
    Views
    558

    I just did a quick CAD rendering is it something...

    I just did a quick CAD rendering is it something like this ?
    124781247912480
    I know the stones not the right colour but usually you would sorce the stone you want then build the ring round that.
  7. Replies
    2
    Views
    107

    12mm seems a bit on the heavy side !

    12mm seems a bit on the heavy side !
  8. Replies
    13
    Views
    379

    Its like going to a posh restaurant and asking...

    Its like going to a posh restaurant and asking how much they pay for beans or asking the cashier at Tesco what they pay for bread. Its irrelevant its the finished item they are buying your hard work,...
  9. Replies
    2
    Views
    134

    Rhino is widely used for Jewellery Cad its not...

    Rhino is widely used for Jewellery Cad its not free but there is a free 3 month trial to see if you like it you can use it after 90 days but it won't save anything. https://www.rhino3d.com/download ...
  10. The ball vise works better under a microscope and...

    The ball vise works better under a microscope and I find it easier to work with. I suppose it depends on your workspace too, I don't have a cutout on my setting bench so the multi vise would stick...
  11. Replies
    5
    Views
    411

    this is a link to a little video of cutting out...

    this is a link to a little video of cutting out sea glass
    https://www.instagram.com/p/BpGzRnej9Pc/

    12443

    I don't have images of the finished pendant but it had 6 or so bits of glass that...
  12. Thread: How about this.

    by josef1
    Replies
    5
    Views
    448

    I think its a bit much for business jewellers...

    I think its a bit much for business jewellers aswell !!
  13. Thread: Hi from Ireland

    by josef1
    Replies
    4
    Views
    266

    Hi Sean and welcome

    Hi Sean and welcome
  14. Replies
    5
    Views
    411

    Hi Sammy Rhino is a great software and lots...

    Hi Sammy

    Rhino is a great software and lots of videos on youtube etc to help you. The CAD learning curve is quite steep but if you have a idea of what you are building that will help. Getting a...
  15. Replies
    18
    Views
    876

    WELCOME TO THE BIRMINGHAM ASSAY OFFICEIMPORTANT...

    WELCOME TO THE BIRMINGHAM ASSAY OFFICEIMPORTANT COVID-19 UPDATE FROM THE BIRMINGHAM ASSAY OFFICE
    While non-essential businesses have been forced to close, Government guidance states other businesses...
  16. Thread: How on earth?

    by josef1
    Replies
    10
    Views
    607

    I think its probs cad and cast the stone will be...

    I think its probs cad and cast the stone will be scanned so the setting can be made as fine as possible but I could be wrong.
  17. Thread: oxidising gold

    by josef1
    Replies
    9
    Views
    524

    I like my sleep Dennis lol

    I like my sleep Dennis lol
  18. Thread: oxidising gold

    by josef1
    Replies
    9
    Views
    524

    Thought I put the wrong link but I didn't and...

    Thought I put the wrong link but I didn't and can't delete this one now lol
  19. Thread: oxidising gold

    by josef1
    Replies
    9
    Views
    524

    https://www.cooksongold.com/Jewellery-Tools/Heimer...

    https://www.cooksongold.com/Jewellery-Tools/Heimerle---Meule-Noirit-Black------Silver-Oxidation-Solution-1-Litre--UN2922-prcode-998-1417&query=oxidising&channel=uk

    I use this to oxidise 9ct gold...
  20. Thread: Eye damage

    by josef1
    Replies
    2
    Views
    259

    With Platinum yes welding goggles are a must but...

    With Platinum yes welding goggles are a must but silver and gold I dont bother with any form of tinted eye protection. That said everyone's different.
  21. Replies
    5
    Views
    720

    You tend to get what you pay for

    You tend to get what you pay for
  22. Replies
    4
    Views
    355

    Royalmail special delivery will insure you upto...

    Royalmail special delivery will insure you upto 2500 I think The other Royal mail services don't insure jewellery as far as I'm aware. On the odd occasion I send abroad I use UPS as I like the...
  23. Replies
    3
    Views
    310

    Tuffnell glass have always been very helpful with...

    Tuffnell glass have always been very helpful with my smiths torch parts https://tuffnellglass.com/contents/en-uk/d100.html obviously try cooksons first but Im not sure if they supply the parts ?
  24. I read somewhere that the borax attacks the...

    I read somewhere that the borax attacks the graphite and this shortens the life of them
  25. I made a CAD 'Uffington Unicorn' its like the...

    I made a CAD 'Uffington Unicorn' its like the horse but about 11% different it would be easier to hand make than CAD though