Casting is essentially the same as sterling, as said above it does not hold its shape well if heated to hi red heat I have never had a problem when annealing, when soldering let it cool a bit before you grab it and pickle
Printable View
Casting is essentially the same as sterling, as said above it does not hold its shape well if heated to hi red heat I have never had a problem when annealing, when soldering let it cool a bit before you grab it and pickle
I melt Argentium scrap and grain all the time, same as any metal really just make sure you keep it annealed when putting it through the mill etc.